ASTM A335 Seamless Ferritic Alloy-Steel Pipe for High-Temperature Service


ASTM A335 P11 SCH80 Ferritic Alloy-Steel Pipe

ASTM A335 P11 SCH80 Ferritic Alloy-Steel Pipe

ASTM A335 Standard Specification for Seamless Ferritic Alloy-Steel Pipe for High-Temperature Service

This specification covers seamless ferritic alloy-steel pipe for high-temperature service. The pipe shall be suitable for bending, flanging (vanstoning), and similar forming operations, and for fusion welding. Grade P2 and P12 steel pipes shall be made by coarse-grain melting practice. The steel material shall conform to chemical composition, tensile property, and hardness requirements. Each length of pipe shall be subjected to the hydrostatic test. Also, each pipe shall be examined by a non-destructive examination method in accordance to the required practices. The range of pipe sizes that may be examined by each method shall be subjected to the limitations in the scope of the respective practices. The different mechanical test requirements for pipes, namely, transverse or longitudinal tension test, flattening test, and hardness or bend test are presented.

1. Scope

1.1 This specification covers nominal wall and minimum wall seamless ferritic alloy-steel pipe intended for high-temperature service. Pipe ordered to this specification shall be suitable for bending, flanging (vanstoning), and similar forming operations, and for fusion welding. Selection will depend upon design, service conditions, mechanical properties, and high-temperature characteristics.

1.2 Several grades of ferritic steels (see Note 1) are covered. Their compositions are given in Table 1.

Note 1: Ferritic steels in this specification are defined as low- and intermediate-alloy steels containing up to and including 10% chromium.

1.3 Supplementary requirements (S1 to S7) of an optional nature are provided. These supplementary requirements call for additional tests to be made, and when desired, shall be so stated in the order together with the number of such tests required.

1.4 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification. The inch-pound units shall apply unless the “M” designation of this specification is specified in the order.

Note 2: The dimensionless designator NPS (nominal pipe size) has been substituted in this standard for such traditional terms as “nominal diameter”, “size”, and “nominal size”.

Mainly Grade of ASTM A335:

ASTM A335 P11, P22, P5, P9, P91, P92

Chemical Composition (%) for the main grade

Grade C Mn P, S, max Si Cr Mo
P11 0.05-0.15 0.30-0.60 0.025 0.50-1.00 1.00-1.50 0.44-0.65
P22 0.05-0.15 0.30-0.60 0.025 0.50 max 1.90-2.60 0.87-1.13
P5 0.15 max 0.30-0.60 0.025 0.50 max 4.00-6.00 0.45-0.65
P9 0.15 max 0.30-0.60 0.025 0.25-1.00 8.00-10.00 0.90-1.10
P91 0.08-0.12 0.30-0.60 0.020/0.010 0.20-0.50 8.00-9.50 0.85-1.05
  V 0.18-0.25 N 0.03-0.07 Ni 0.40 max Al 0.02 max Nb 0.06-0.10 Ti 0.01 max
P92 0.07-0.13 0.30-0.60 0.020/0.010 0.50 max 8.50-9.50 0.30-0.60
  V 0.15-0.25 N 0.03-0.07 Ni 0.40 max Al 0.02 max Nb 0.04-0.09 W 1.50-2.00
        B 0.001-0.006 Ti 0.01 max Zr 0.01 max

 

Standard Grade C Mn Si P S Cu Ni Cr Mo V Al N Nb,Ti,B,As and W
ASTM A335 P1 0.10 0.20 0.30 0.80 0.10 0.50 ≤0.025 ≤0.025       0.44 0.65        
ASTM A335 P2 0.10 0.20 0.30 0.60 0.10 0.30 ≤0.025 ≤0.025     0.50 0.81 0.44 0.65        
ASTM A335 P5 ≤0.15 0.30 0.60 ≤0.50 ≤0.025 ≤0.025     4.00 6.00 0.45 0.65        
ASTM A335 P11 0.05 0.15 0.30 0.60 0.50 1.00 ≤0.025 ≤0.025     1.00 1.50 0.44 0.65        
ASTM A335 P12 0.05 0.15 0.30 0.61 ≤0.50 ≤0.025 ≤0.025     0.80 1.25 0.44 0.65        
ASTM A335 P22 0.05 0.15 0.30 0.60 ≤0.50 ≤0.025 ≤0.035     1.90 2.60 0.87 1.13        
ASTM A335 P91 0.08 0.12 0.30 0.60 0.20 0,50 ≤0.020 ≤0.010   ≤0.40 8.00 9.50 0.85 1.05 0.18 0.25 ≤0.02 0.03 0.07 Ti ≤ 0.01
ASTM A335 P92 0.07 0.13 0.30 0.60 ≤0.50 ≤0.020 ≤0.010   ≤0.40 8.50 9.50 0.30 0.60 0.15 0.25 ≤0.040 0.03 0.07 B 0.001-0.006 W 1.5-2.00
ASTM A335 P112 0.07 0.14 0.70≤ ≤0.50 ≤0.020 ≤0.010 0.30 1.70 ≤0.50 10.00 12.00 0.25 0.60 0.15 0.30 ≤0.040 0.040 0.100 B 0.0005-0.0005 W 1.50-2.50 Cb 0.40-0.10

 

Mechanical Properties

Standard Grade

Heat 

Treatment

Pour Point Re min. (Mpa)

Tensile

Strength

Elongation  (%) Impact (J)

Application 

Temperature(°C)

t 0-16 mm t 16-40 mm t 40-65 mm
ASTM A335 P1 N 205 205 205 ≥ 380 30   530
ASTM A335 P2 Z 205 205 205 ≥ 380 30   560
ASTM A335 P5 Z 205 205 205 ≥ 415 30   600
ASTM A335 P11 Z 205 205 205 ≥ 415 30   560
ASTM A335 P12 Z 220 220 220 ≥ 415 30   560
ASTM A335 P22 Z 205 205 205 ≥ 415 30   560
ASTM A33

5

P91 Z 415 415 415 ≥ 585 20   650
ASTM A335 P92 Z 440 440 440 ≥ 620 20   650
ASTM A335 P122 Z 400 400 400 ≥ 620 20   650

 

<< Back to Steel pipes


Share to: LinkedIn Twitter Facebook Google


Related Tags: Alloy Steel Pipe (6)  ASTM A335 Steel Pipe (1)  

ASTM A335 Seamless Ferritic Alloy-Steel Pipe for High-Temperature Service Related Posts :
ASTM A53 Pipe, Steel, Black and Hot-Dipped, Zinc-Coated, Welded and Seamless
DIN 17175 seamless steel pipe for elevated temperature St35.8, St45.8, 17Mn4, 19Mn5, 15Mo3, 13CrMo44
JIS G3452 Carbon Steel Pipes for Ordinary Piping
DIN 1629 Seamless tubes,pipes circular unalloyed steel
Nf a49-145-78 Hot Finished Welded Pipes Suitable For Threading
API 5L Line Pipe
GB/T8163 Seamless steel tubes pipes for liquid service
EN 10216 Seamless steel tubes for pressure purposes
ASTM A197 Cupola Malleable Iron
DIN 2448 Seamless and welded steel pipes-EN 10220

Haihao Group Twitter haihao group youtube haihao group facebook haihao group linkedin